What is stainless steel 201 (UNS S20100)1.4372?
201 ruostumaton teräs, with certain acid and alkali resistance, high density, no bubbles, no pinholes, etc. It is a high-quality material for producing various case and strap bottom cover. Mainly used for decorative tubes, industrial tubes, some shallow stretched products.
Tyyppi 201 is normally limited to nearly flat or shallow drawn products such as automotive trim, builder’s hardware comprised of window and door components, flatware, rapid transit cars and trailers.
201 ruostumaton teräs 1.4372 Finished Products Form
- Arkki
- Strip
- coils
- foils
Hakemuksia varten 201 ruostumaton teräs
Typical applications for Types 201 contains cookware, hose clamps, piston rings, transit car structural member, transit car roofing/siding, thermal window spacers, airbag containers, and truck trailer posts and door frames.
Earvosanan ekvivalentteja 201
| EU SISÄÄN | USA – | Japani HÄN | Ranska AFNOR |
| X12CrMnNiN17-7-5 | 201 | SUS201 | Z12CMN17-07Az |
Sävellys ulottuu 201 luokka ruostumatonta terästä
| ITEM | NI | CR | CU | MN | SI | C | N | P | S |
| Min | 0.80 | 14.00 | 1.30 | 8.00 | === | === | === | === | === |
| Max | 1.30 | 17.00 | 2.00 | 10.00 | 1.00 | 0.15 | 0.25 | 0.06 | 0.03 |
Mekaaniset ominaisuudet
Mechanical property requirements for annealed product as specified in ASTM A240 and ASME SA24
| Property | 201 |
| Tuottovoima, min. (ksi) | 45 |
| Vetolujuus, min. (ksi) | 95 |
| Pidentymä, min. (%) | 40 |
| Kovuus, max. (Rb) | 100 |
Mechanical property requirements for cold worked flat rolled products as specified in ASTM A666
| Condition | Tuottovoima (ksi) min. | Vetolujuus (ksi) min. | Pidentymä % min. sisään 2 sisään. | |
| <0.015 sisään. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Fyysiset ominaisuudet
| Tiheys, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Lämmönjohtokyky, Btu/ft hr ˚F | 9.4 |
| Ominaislämpö, Btu/lb ˚F | 0.12 |
| Sähkövastus, Microohm-in | 27.0 |
Fabrication
Tyyppi 201 Stainless Steel can be fabricated by bench forming, roll forming and brake bending in much the same manner as Type 301. However, because of its higher strength, it may exhibit greaterspringback. This material can be drawn similarly to Type 301 in most drawing operations if more power is used and the hold-down pressure is increased.
Korroosionkestävyys
The general level of corrosion resistance of Type 201 is similar to Type 301. Type 201 should perform adequately as a replacement for Type 301, except in the most demanding environments. The scalng resistance of Type 201 is less than that of Type 301. Tyyppi 201 resists destructive scaling up to about 1550°F
(843°C), about 100°F (56°C) less than Type 301.
Hot Working
Arvosana 201 stainless steel is hot worked at 1149-1232°C (2100-2250°F).
Hehkutus
Arvosana 201 stainless steel is annealed at 1010-1093°C (1850-2000°F). Temperature should not be exceeded above 2000°F in order to avoid scaling. It is rapidly cooled to prevent crystallization of carbides.
Hitsattavuus
The austenitic class of stainless steels is generally considered to be weldable by the common fusion and resistance techniques. Special consideration is required to avoid weld “hot cracking” by assuring formation of ferrite in the weld deposit. As with other chrome-nickel austenitic stainless steel grades where carbon is not restricted to 0.03% or below, the weld heat affected zone may be sensitized and subject to intergranular corrosion in some environments.This particular alloy is generally considered to have poorer weldability to the most common alloy of this stainless class, Type 304L Stainless Steel. When a weld filler is needed, AWS E/ER 308 is most often specified. Tyyppi 201 Stainless Steel is well known in reference literature and more information can be obtained in this way.