254 SMO®Stainless steel (UNS31254)

What is 254 SMO®?

254 SMO® is a stainless steel was initially created to utilize in seawater and other aggressive chloride-bearing situations. This grade includes a very high end austenitic stainless steel; mainly comprised within 17.5% to 18.5% nickel, 19.5% SY 20.5% chromium, 6% to 6.5% molybdenum and .18% to .22% nitrogen.These particular levels of Cr, In, Mo, and N in this “super austenitic” chemical makeup allow 31254 to join impact toughness resistance to corrosion cracking, with pitting and crevice corrosion resistance.The result is strength of almost double that of 300 series stainless steels.

UNS S31254 is treated as a “6% Moly” grade because of the molybdenum content; ny 6% Moly family has the ability to withstand high temperatures and keep up strength under volatile conditions. This grade has surpassed its unique expectation and covered into many different industries demonstrating helpfulness owing to its high level of molybdenum amount other elements, which allows 31254 to be utilized effectively as a part of different applications such as flue gas desulfurization and chemical environments.

 254 SMO® Products Form

• Round, Square, Hexagon ,Flat Bars & Wires
• miray volo / Welded Pipes
• miray volo / Welded Tubes
• Hot & Cold Rolled Plates & Sheets
• Forged Bars
• Forged Flanges
• Butt-Weld Pipe Fittings
• Socket-Weld/Forged Pipe Fittings
• Machined Components
• Ferrule Compression Fittings
• Welding Consumables
• Common Manufacturi

Applications for 254 SMO®

1) Ocean: marine structures in the sea environment, seawater desalination, marine aquaculture, seawater heat exchange, etc.;

2) Environmental Protection: flue gas desulfurization device for thermal power generation, wastewater treatment, etc.;

3) Energy: atomic power generation, comprehensive utilization of coal, and ocean wave power generation.;

4) Indostria Petrokimia: refining, chemical equipment;

5) Food: salt making, soy sauce brewing, etc.;

6) High concentration chloride ion environment: paper industry, various bleaching devices;

7) Others.

Equivalents of 254 SMO®

Malagasy	antsika	WERKSTOFF NR.	AFNOR	IN	izy	SIS	GOST
SMO 254	S31254	1.4547	Z1 CNDU 20.18.06Az	X1CrNiMoCuN20-18-7	–	2378	–

Composition ranges for 254 SMO®

%	C	Cr	Mn	Mo	N	In	t	SY	S
254 SMO	0.02 max	min: 19.5 max:20.0	1.00 max	min: 6.0 max: 6.5	min: 0.18 max: 0.20	min: 17.5 max: 18.0	0.03 max	0.80 max	1.01 max

Mechanical Properties

Properties	mimetatra	amperora
Faharetana amin'ny sintona	680 MPa	98600 psi
hery manome	300 MPa	43500 psi
Modulus of elasticity	195 GPa	28300 ksi
Shear modulus	75 GPa	10900 ksi
Poisson’s ratio	0.30	0.30
Elongation at break	50 %	50 %
hamafin'ny, Brinell	210	210

Physical Properties

	Units	Temperature in °C
hakitroky	8.0 g/cm³	Room
Specific Heat	0.12 Kcal/kg.C	22°
Melting Range	1320 – 1390 °C	–
Modulus of Elasticity	195 KN/mm²	20°
Electrical Resistivity	85 µΩ.cm	Room
Coefficient of Expansion	16.0 µm/m °C	20 – 100°
Thermal Conductivity	14.0 W/m °K	20 °

Ny fanoherana ny harafesina

• Excellent resistance to pitting and crevice corrosion due to its high chromium, molybdenum, and nitrogen content
• Has a very low carbon content, which means there is very little risk of carbide precipitation during heating
• Possesses very good resistance in water containing chlorides, therefore, it is suitable for use in seawater as it can be exposed to it for prolonged periods without suffering from crevice corrosion

Fitsaboana hafanana

Stainless steel grade 254 SMO™ does not respond to heat treatment. Hardening is possible only through cold reduction.

Annealing

2100-2200 F (1149-1204 C), followed by a water quench.

Hardening

This alloy does not harden by heat treating. High properties might just be acquired through cold reduction

Hot Working

While cold forming is recommended wherever feasible, forging, upsetting and other operations can be performed at 1800-2100 F. Temperatures above this range will cause scaling and a reduction in the workability of the material. Post-process annealing is required to re-attain maximum corrosion resistant properties.

Mangatsiaka miasa

Most common cold work methods are successful with this alloy. It should be understood however that the material will be more difficult to work than other austenitic stainless steels due its high work hardening rate. The resulting hardening will, however, produce increases in strength and toughness which may be of value in the finished product.

manorina

This is a highly alloyed material and the recommended forging temperature range is 2370/1920ºF (1300/1050ºC), followed by a solution anneal at 2100ºF (1150ºC) minimum temperature.

Machinability

Stainless steel grade 254 SMO™ is quite tough to machine due to the extremely high work hardening rate and lack of sulfur content; however using sharp tools,

overpowered machine tools, positive feeds, good amount of lubrication, and slow speeds tend to provide good machining results.

Weldability

The chemical analysis of 254 SMO grade is such that both ferrite and austenite are formed on cooling from welding, giving resistance to hot cracking. A postweld anneal is recommended, as is consultation with the product manufacturer regarding welding parameters.