ASTMSA213StainlessSteelSeamlessTubeSupplierAndStockistInChina

Brezšivna cev iz nerjavečega jekla/

Brezšivna cev iz nerjavečega jekla ASTM SA213

Ime:Brezšivna cev iz nerjavečega jekla

Velikost:1/8"-36"inch DN5~DN1000,OD6mm-OD1020mm

Material:Stainless Steel SS 304/SS316L

Connect Type:WELDING/THREAD

Work Pressure:1.6Mpa/2.5mpa/5mpa/10mpa

Thickness range:SCH 5, SCH10, SCH 40, SCH 80, SCH 80S, SCH 160, SCH XXH, SCH XXS, SCH XS

Površinsko obdelavo:Pickling/Polished/Bright Anealing/EP/MP/Annealed and Pickled (AP), Polished, Bright Annealed (BA), Cold Drawn, MF

Finished conditionBrezhibno / Erw / Varjeno / Izdelano / CDW / CDS / DOM / CEW / 100% X Ray Welded

Aplikacija:Fluid contrl pipeline system

Model Number ASTM A213

Los:Wenzhou,zhejiang

Standard:EU,ON, AiSi, ASTM, OD ,GOST,IN ,ASTM A213, ASTM A312, ASTM A269, Astm 270,ASTM A778, ASTM A554, ASTM A249, ASTM A269, ASTM A270, ASTM A789, OD 17456, DIN17457, OD 17459, JIS G3459, JIS G3463, GOST9941, EN10216, BS3605, GB13296,Acord requiment cad drawing

Brand:OEM Ava

Technics:Presselible

Usage:Round pipe

Paket:Standard export pakage

Cena:Negotiate 1000~12000 usd/ton

Dostava:Količina Accord

Certificate

ABS, GL, DNV, NK, PED, AD2000, GOST9941-81, CCS, ISO 9001-2008

Production ability1000tons per month

  • Podrobnosti o izdelku

ASTM A213 je standardna specifikacija za brezhibno feritsko in austenitno kotel z izlivko, Pregret, in cevi za toplotno izmenjavo. Ta specifikacija zajema minimalno debelino stene, brezhibno, in hladno narisane jeklene cevi za cevaste toplotne izmenjevalnike, kondenzatorji, in podoben aparat za prenos toplote.

Dimenzija brezhibne cevi iz nerjavečega jekla ASTM A213 se lahko razlikuje glede na uporabo in je navedena spodaj:

1. Zunanji premer: 6.00 mm do 1020 mm
2. Debelina stene: 0.50 mm do 75.00 mm
3. Dolžina: Največ 12.5 metri

Ta specifikacija se običajno uporablja v visokotemperaturnih servisnih aplikacijah, kot so pregrevalci in ponovni ogrevalci v elektrarnah, Kemična in petrokemična industrija, in rafinerije. Cev je primerna tudi za ogrevalne elemente, kondenzatorji, Kriogene posode, in podobne aplikacije. Poleg tega, Cev ASTM A213S so primerni za jedko in visokotemperaturno uporabo, kjer sta potrebna visoka trajnost in odpornost na obrabo.

V povzetku, the ASTM A213 Brezšivna cev iz nerjavečega jekla je zasnovan za visokotemperaturne aplikacije v različnih panogah in ponuja trajno in zanesljivo rešitev za ogrevalne in hladilne sisteme, ki potrebujejo visoko trdnost, Korozijska odpornost, in toplotna učinkovitost.

ASTM A213 Nerjavno jeklo brezšivna cev Proces izdelave

ASTM A213 je specifikacija za brezhibno feritsko in austenitno kotel z izlivko, Pregret, in cevi za toplotno izmenjavo. Brezšivne cevi iz nerjavečega jekla ki ustrezajo tej specifikaciji, se uporabljajo za visokotemperaturno storitev in se proizvajajo z različnimi proizvodnimi procesi. Tu je splošen pregled Proces izdelave nerjavečega jekla ASTM A213 brezšivne cevi:

1. Izbira surovin: Prvi korak v proizvodnem procesu je izbrati ustrezne surovine, kar je v tem primeru kakovostno nerjaveče jeklo.

2. Taljenje in igranje: Surovine se stopijo v peči in vržejo v gredice ali cvetenja.

3. Vroče valjanje: Igralske gredice ali cvetove se nato vroče valjajo brezšivne cevi z uporabo mlina ali mlina za vtič.

4. Hladna risba: Vroče valjane cevi se nato potegnejo skozi vrsto matric, da zmanjšajo premer in debelino stene. Ta postopek je znan kot hladna risba.

5. Toplotno obdelavo: Cevi se nato toplotno obdelajo, da izboljšajo njihove mehanske lastnosti in odstranijo morebitne preostale napetosti.

6. Zaključek: Cevi se nato končajo z rezanjem, Čiščenje, razbremenitev, in testiranje, da se zagotovi, da izpolnjujejo zahtevane specifikacije.

7. Končni pregled in embalaža: Končne cevi so doživeli končni pregled in jih nato zapakirajo in odposlane do cilja.

Na splošno, Proces proizvodnje ASTM A213 brezšivne cevi iz nerjavečega jekla vključuje kombinacijo taljenja, kasting, vroče valjanje, Hladna risba, toplotno obdelavo, zaključek, in pregledni postopki za izdelavo cevi, ki ustrezajo potrebnim specifikacijam za visokotemperaturno storitev.

ASTM A213 Nerjavno jeklo brezšivna cev Specifikacija

ASTM A213 je specifikacija za brezhibno feritsko in austenitno kotel z izlivko, Pregret, in cevi za toplotno izmenjavo. Ocene materiala, zajete v tej specifikaciji, vključujejo T2, T5, T9, T11, T12, T22, T91, in T92.

Brezšivne cevi, izdelane v skladu s to specifikacijo, so namenjene visokotemperaturnim in visokim pritiskom. Cevi morajo biti pred uporabo toplotno obdelane za izboljšanje njihovih mehanskih lastnosti.

Cevi morajo opraviti tudi različne teste, vključno z dimenzijskim pregledom, vizualni pregled, Hidrostatično ali nedestruktivno električno testiranje, Eddy toka testiranja, in testi za bliskavico in sploščitve.

Velikosti cevi, ki so na voljo v skladu s to specifikacijo, segajo od 1/8″ NB do 5″ Nb (10.3mm do 127 mm OD) in od 0,015″ do 0,500″ debelina. Dolžine cevi so na splošno 6 metri ali po zahtevah kupcev.

ASTM A213 nerjaveče Specifikacija jeklene brezhibne cevi zajemajo različne vrste nerjavečega jekla ocene, vključno z austenitnimi in feritskimi jekla. Nekatere najpogosteje uporabljene ocene vključujejo 304, 304L, 316, 316L, 321, in 347. Te cevi se uporabljajo predvsem v različnih aplikacijah, vključno s petrokemijskim, proizvodnja električne energije, in na morju vrtanja.

ASTM SA213 brezhibna nanos cevi iz nerjavečega jekla

ASTM SA213 brezhibna cev iz nerjavečega jekla se pogosto uporablja v različnih panogah, kot so:

1. Petrokemična industrija
2. Raziskovanje nafte in plina
3. Kemična obdelava
4. Predelava hrane
5. Farmacevtska industrija
6. Avtomobilska industrija
7. Proizvodnja električne energije
8. Vesoljska industrija
9. Medicinska oprema
10. Morska industrija

Te brezšivne cevi se obsežno uporabljajo v visokotemperaturnih in visokotlačnih aplikacijah zaradi odlične odpornosti proti koroziji, oksidacija, in ekstremne temperaturne pogoje. Najdejo uporabo v cevovodih za prenos vročih in jedkih tekočin, kot cevi za toplotni izmenjevalnik, in v kotlovskih ceveh za visokotlačne pare. They are also widely used in industries that require hygienic and sterile conditions, such as the food and pharmaceutical industries. Furthermore, these tubes are essential in the construction of aircraft and components that encounter extreme environments, such as rocket exhausts and turbines.

ASTM A213 Nerjavno jeklo brezšivna cev Properties

Stainless steel grades: TP304, TP304L, TP316, TP316L, TP347
Dimensions: Outer diameter range from 6mm to 323mm, wall thickness range from 0.5mm to 30mm, length up to 20 metri
– Toplotno obdelavo: Annealed, bright annealed, pickled, polished
– Površinska obdelava: Mill finish, polished finish, smooth finish, brushed finish
– Toleranca: OD tolerance +/- 0.005 inch, wall thickness tolerance +/- 10%
Corrosion resistance: Excellent resistance to corrosion in a wide range of environments, including acidic, alkaline, and chloride-containing environments
High temperature strength: Capable of withstanding high temperatures up to 1150°C
Applications: Used in various industries such as chemical processing, food processing, Farmacevtski izdelki, proizvodnja električne energije, oil and gas, pulp and paper, and heat exchangers.

Ocena Natezno trdnost Yield Point Raztezek Trdota(HRB) Solution Temperature
Min, Mpa Min, Mpa Min, % Max Rockwell Min, OC,
TP304 515 205 35 90 1040
TP304L 485 170 35 90 1040
TP316 515 205 35 90 1040
TP316L 485 170 35 90 1040
TP321 515 205 35 90 1040

ASTM A213 Natezna in trdota brezhibne cevi

Izdelek Ocena UNS Designation Natezno trdnost Moč tečenja Elongation In 2 In. Or 50 Mm Trdota Trdota,
Min Ksi [MPa] Min Ksi [MPa] Min, % Max Brinell/Vickers Max Rockwell
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP304 S30400 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP304L S30403 70 [485] 25 [170] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP304H S30409 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP304N S30415 80 [550] 35 [240] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP310S S31008 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP310H S31009 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP316 S31600 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP316L S31603 70 [485] 25 [170] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP316H S31609 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP316Ti S31635 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP317 S31700 75 [515] 30 [205] 34 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP317L S31703 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP321 S32100 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP321H S32109 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP347 S34700 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP347H S34709 75 [515] 30 [205] 35 192HBW/200Hv 90HB
Brezšivna cev iz nerjavečega jekla ASTM SA213 TP444 S44400 60 [415] 40 [275] 20 217 HBW/230HV 96HB

ASTM SA213 SA213 Grafikon dimenzij brezhibne cevi

The dimensions of ASTM SA213 stainless steel seamless tube vary depending on the specific grade and size. Below are the general dimensions for some commonly used grades:

TP304/304L: Outer diameter (Od) ranges from 6.00mm to 1020mm, debelina stene (WT) ranges from 0.70mm to 8.00mm.
TP316/316L: OD ranges from 6.00mm to 114.3mm, WT ranges from 0.70mm to 10.00mm.
TP321/321H: OD ranges from 6.00mm to 114.3mm, WT ranges from 0.89mm to 10.00mm.
TP347/347H: OD ranges from 6.00mm to 114.3mm, WT ranges from 0.89mm to10.00mm.

It is important to consult the specific ASTM SA213 standard and manufacturer’s datasheet for accurate dimensions of a particular product.

Zunanji premer Zunanji premer BWG BWG BWG BWG BWG BWG BWG BWG
25 22 20 18 16 14 12 10
WT/mm WT/mm WT/mm WT/mm WT/mm WT/mm WT/mm WT/mm
0.508 0.71 0.89 1.24 1.65 2.11 2.77 3.4
mm inch kg/m kg/m kg/m kg/m kg/m kg/m kg/m
6.35 1/4 0.081 0.109 0.133 0.174 0.212
9.53 3/8 0.126 0.157 0.193 0.257 0.356 0.429
12.7 1/2 0.214 0.263 0.356 0.457 0.612 0.754
15.88 5/8 0.271 0.334 0.455 0.588 0.796 0.995
19.05 3/4 0.327 0.405 0.553 0.729 0.895 1.236
25.4 1 0.44 0.546 0.75 0.981 1.234 1.574 2.05
31.75 1-1/4 0.554 0.688 0.947 1.244 1.574 2.014 2.641
38.1 1-1/2 0.667 0.832 1.144 1.514 1.904 2.454 3.233
44.5 1-3/4 1.342 1.774 2.244 2.894 3.5
50.8 2 1.549 2.034 2.574 3.334 4.03
63.5 2-1/2 1.949 2.554 3.244 4.214 5.13
76.2 3 2.345 3.084 3.914 5.094 6.19
88.9 3-1/2 2.729 3.609 4.584 5.974 7.27
101.6 4 4.134 5.254 6.854 8.35
114.3 4-1/2 4.654 5.924 7.734 9.43
Tolerance ASTM A213, Zunanji premer, Stena brez gostega in dolžine
Hladno končane brezhibne cevi
Od OD Tolerance OD Tolerance WT Tolerance WT Tolerance Length Tolerance Length Tolerance
Mm Over Under Over Under Over Under
Under 25.4 0.1016 0.1016 +20 -0 3.175 0
25.4-38.1 Incl 0.1524 0.1524 +20 -0 3.175 0
38.1-50.8 Excl 0.2032 0.2032 +22 -0 3.176 0
50.8-63.5 Excl 0.254 0.254 +22 -0 4.46 0
63.5-76.2 Excl 0.3048 0.3048 +22 -0 4.76 0
76.2-101.6 Incl 0.381 0.381 +22 -0 4.76 0
101.6-190.5 Incl 0.381 0.635 +22 -0 4.76 0
190.5-228.6 Incl 0.381 1.143 +22 -0 4.76 0
Vroče končane brezšivne cevi
Zunanji premer, Mm Toleranca, Mm
OD≤101.6 +0.4/-0.8
101.6<OD≤190.5 +0.4/-1.2
190.5<OD≤228.6 +0.4/-1.6
Debelina vroče valjane stene & Toleranca
Zunanji premer, Mm Toleranca, %
OD≤101.6, WT≤2.4 +40/-0
OD≤101.6, 2.4<WT≤3.8 +35/-0
OD≤101.6, 3.8<WT≤4.6 +33/-0
OD≤101.6, WT>4.6 +28/-0
Od>101.6, 2.4<WT≤3.8 +35/-0
Od>101.6, 3.8<WT≤4.6 +33/-0
Od>101.6, WT>4.6 +28/-0
ASTM A213 tolerance debeline stene

ASTM A213 specifies Minimum wall thickness, namely, there is no mill undertolerance, only overtolerance, unless specified as average wall thickness is requied, permissible variations from the specified average wall thickness shall be +/-10 % of the specified average wall thickness for cold formed tubes.

Seamless tubing furnished to this specification shall conform to the requirements of Specification ASTM A1016/A1016M, including any supplementary requirements.

ASTM SA213 stainless steel seamless tube Chemical composition
Ocena C in Mn Kr notri Mo S p Fe
Max, % Max, % Max, % % % % Max, % Max, % %
TP304 0,08 1,0 2 18 – 20 8 – 11 0,03 0,045 Bal
TP304L 0,035 1,0 2 18 – 20 8 – 12 0,03 0,045 Bal
TP316 0,08 1,0 2 16 – 18 11 – 14 2 – 3 0,03 0,045 Bal
TP316L 0,035 1,0 2 16 – 18 10 – 14 2 – 3 0,03 0,045 Bal
TP321 0,08 1,0 2 17 – 19 9 – 12 0,03 0,045 Bal

Prejšnji:

+86-577-85980211

v živo:ericjiwz

+8615968750098

306208216

Pustite sporočilo

    Vsebine te strani ne morete kopirati